BS 2782-1 塑料热老化后延展性测定

放大字体  缩小字体 发布日期:2020-03-26   浏览次数:46  分享到: 分享到腾讯微博
 
BS 2782-1  塑料热性能试验方法-标准名称
BS 2782-1 Methods of testing plastics – Part1:Thermal properties-Method 131B:Determination of extensibility after heat ageing of flexible polyvinyl chloride sheet
BS 2782-1塑料试验方法。第1部分:热性能-方法131B:柔性聚氯乙烯板热老化后延展性的测定
 
BS 2782-1  塑料热性能试验方法-标准简介
 
BS 2782-1这种方法确定了薄膜或薄板产生裂纹的特征温度,作为其低温性能的指导。冷裂纹温度不应被视为与材料的低温极限相同,因为受每种材料的使用条件的影响。
 
BS 2782-1This method determines a characteristic temperature at which cracks are produced in film or thin sheeting, as a guide to its low-temperature performance.The cold crack temperature should not be considered identical with the low-temperature limit for materials in actual service, since this is influenced by the conditions of service in each case. The maximum thickness depends on the stiffness of the material and the ability of the hammer to flatten the loop of material at the test temperature, but is about 1 mm for flexible sheeting.It is known that unsatisfactory results are sometimes obtained with thin polished plasticized PVC sheeting and PVC sheeting having a low plasticizer content.
 
BS 2782-1  塑料热性能试验方法-相关标准
BS 2782 Pt.2 Method 250A-1976 塑料的试验方法.第2部分:电气性能.试验方法250A:薄膜抗静电性.电荷减少法
 

  详情请咨询
  防火资源网-阻燃防火测试中心
  电话:(+86)0592-5056213
  传真:(+86)0592-5105807
  邮件:firetest@firetc.com

凡注明"防火资源网"的所有作品,由<防火资源网>整理编辑,任何组织未经<防火资源网>及其拥有者授权,不得复制、转载、摘编或利用其它方式应用于任何商业行为。

 
 
[ 防火测试中心搜索 ]  [ ]  [ 告诉好友 ]  [ 打印本文 ]  [ 关闭窗口 ]  [ 返回顶部 ]

 

 
 
推荐防火测试
推荐图文
点击排行
 
 
网站首页 | 广告服务 | 关于我们 | 联系方式 | 服务协议 | 版权声明 | 网站地图 | 友情链接 | 网站留言 | 旧版本 | 闽ICP备09009213号
©2019-2021 FIRETC.COM All Rights Reserved   备案号:闽ICP备09009213号-1在线客服 点击QQ交谈/留言 点击QQ交谈/留言