基础创新PC LEXAN ML6411 产品特性：无溴无卤5VA级防火阻燃（2mm 能达到5VB），良好的流动性，良好的抗冲击性，中等耐热性，具备光屏蔽能力
我公司提供的产品均为正牌塑胶原料，品质保证，货源稳定，送货上门，可免费提供官方物性表、UL黄卡，并随货提供RoHS报告、SGS报告等，索取权威资料请致电13268582149
PC ML6411 物性表：
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.30 | % | ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 2 | 2500 | MPa | ASTM D638 |
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength 3 (Yield) | 62.0 | MPa | ASTM D638 |
| Tensile Stress (Yield) | 62.0 | MPa | ISO 527-2/50 |
| Tensile Strength 3 (Break) | 54.0 | MPa | ASTM D638 |
| Tensile Stress (Break) | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation 3 (Yield) | 5.0 | % | ASTM D638 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Tensile Elongation 3 (Break) | 100 | % | ASTM D638 |
| Tensile Strain (Break) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 4 (50.0 mm Span) | 2600 | MPa | ASTM D790 |
| Flexural Modulus 5 | 2350 | MPa | ISO 178 |
| Flexural Strength 5, 6 | 90.0 | MPa | ISO 178 |
| Flexural Strength 4 (Yield, 50.0 mm Span) | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 150 | J/m | |
| 23°C | 900 | J/m | |
| Notched Izod Impact Strength 7 | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Instrumented Dart Impact (23°C, Total Energy) | 72.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 128 | °C | ASTM D648 |
| Heat Deflection Temperature 8 (0.45 MPa, Unannealed, 100 mm Span) | 125 | °C | ISO 75-2/Be |
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 114 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 119 | °C | |
| Heat Deflection Temperature 8 (1.8 MPa, Unannealed, 100 mm Span) | 115 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 134 | °C | ASTM D1525 9 |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ISO 306/B50 |
| -- | 135 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-40 to 40°C) | 0.000077 | cm/cm/°C | ASTM E831 |
| CLTE - Flow (-40 to 40°C) | 0.000070 | cm/cm/°C | ISO 11359-2 |
| CLTE - Transverse (-40 to 40°C) | 0.000059 | cm/cm/°C | ASTM E831 |
| CLTE - Transverse (-40 to 40°C) | 0.000070 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
| Volume Resistivity | > 1.0E+15 | ohm·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 27 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating - UL | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
PC 基础创新塑料(美国) 101R 通用注塑级本色 加脱模剂，无卤
PC 基础创新塑料(美国) 103R-111 通用注塑级本色 添加脱模剂、紫外线稳定剂、无卤。
PC 基础创新塑料(美国) 121R 通用注塑级本色 加脱模剂,无卤
PC 基础创新塑料(美国) 131 通用注塑级本色 无卤
PC 基础创新塑料(美国) 131R-111 通用注塑级 一般级,超高粘度
PC 基础创新塑料(美国) 141R 通用注塑级本色 加脱模剂，无卤
PC 基础创新塑料(美国) 141R-111 通用注塑级 一般级,UL 94HB，一般射出成形用，低粘度
PC 基础创新塑料(美国) 141R-701 通用注塑级 通用级,UL 94HB，一般射出成形用，低粘底
PC 基础创新塑料(美国) 143 通用注塑级本色 加紫外线稳定剂，无卤
PC 基础创新塑料(美国) 143R 通用注塑级本色 加脱模剂，紫外线稳定剂，无卤
PC 基础创新塑料(美国) 144R 通用注塑级本色 加脱模剂。
PC 基础创新塑料(美国) 163 通用注塑级本色 加脱模剂、紫外线稳定剂，良好的可加工性，中等粘度
PC 基础创新塑料(美国) 2034E 通用注塑级