德国拜耳PC/ABS Bayblend FR2000 产品特性：5VA阻燃，尺寸稳定，良好的颜色稳定性，高刚性，耐低温冲击，高耐热性，良好的可加工性，热稳定性良好，用于家电，汽车应用，草坪和园林设备
我公司提供的产品均为正牌塑胶原料，品质保证，货源稳定，送货上门，可免费提供官方物性表、UL黄卡，并随货提供RoHS报告、SGS报告等，索取权威资料请致电13268582149
PC/ABS FR2000 物性表：
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Density | 1180 | kg/m³ | ISO 1183 2 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 26 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (240°C/5.0 kg) | 26.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow 3 | 0.50 to 0.70 | % | ASTM D955 |
| Molding Shrinkage - Across Flow 3 | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (Saturation, 23°C, 3.18 mm) | 0.50 | % | ISO 62 |
| Water Absorption (Saturation) | 0.50 | % | ISO 62 2 |
| Water Absorption (Equilibrium, 23°C, 3.18 mm, 50% RH) | 0.20 | % | ISO 62 |
| Water Absorption (Equilibrium) | 0.20 | % | ISO 62 2 |
| Spiral Flow Length (254°C, 2.54 mm) | 762 | mm | |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 4 (23°C) | 2700 | MPa | ASTM D638 |
| Tensile modulus | 2700 | MPa | ISO 527-2 2 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 2 |
| Tensile Strength 5 (Break, 23°C) | 44.8 | MPa | ASTM D638 |
| Tensile Elongation 5 (Yield, 23°C) | 4.0 | % | ASTM D638 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 2 |
| Tensile Elongation 5 (Break, 23°C) | > 50 | % | ASTM D638 |
| Nominal strain at break | > 50 | % | ISO 527-2 2 |
| Flexural Modulus (23°C) | 2690 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain, 23°C) | 95.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
| Notched Izod Impact (23°C, 3.18 mm) | 430 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | No Break | ASTM D4812 | |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (0.45 MPa) | 90.0 | °C | ISO 75-2 2 |
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 82.2 | °C | ASTM D648 |
| Deflection Temperature Under Load (1.8 MPa) | 80.0 | °C | ISO 75-2 2 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 6 |
| Vicat Softening Temperature (50°C/h, B (50N)) | 92.0 | °C | ISO 306 2 |
| CLTE - Flow | 0.000077 | cm/cm/°C | ASTM D696 |
| CLTE - Flow | 0.000076 | cm/cm/°C | ISO 11359-2 2 |
| CLTE - Transverse | 0.000077 | cm/cm/°C | ASTM D696 |
| CLTE - Transverse | 0.000080 | cm/cm/°C | ISO 11359-2 2 |
| Electrical | Nominal Value | Unit | Test Method |
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohm·cm | IEC 60093 |
| Relative Permittivity (100 Hz) | 3.20 | IEC 60250 2 | |
| Relative Permittivity (1 MHz) | 3.10 | IEC 60250 2 | |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | ||
| 23°C, 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 0.0050 | ||
| 23°C, 1 MHz | 0.0070 | ||
| Dissipation Factor (100 Hz) | 0.0050 | IEC 60250 2 | |
| Dissipation Factor (1 MHz) | 0.0070 | IEC 60250 2 | |
| Comparative Tracking Index (Solution A) | 400 | V | IEC 60112 |
| Comparative tracking index | 500 | IEC 60112 2 | |
| Electric Strength (23°C) | 30 | kV/mm | IEC 60243-1 |
| Electric strength | 30 | kV/mm | IEC 60243-1 2 |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating - UL | UL 94 | ||
| 2.00 mm | 5VB | ||
| 3.00 mm | 5VA |
PC/ABS 韩国LG EU-5000 通用注塑级
PC/ABS 韩国LG EU-5000G 通用注塑级
PC/ABS 韩国LG EU-5007 通用注塑级
PC/ABS 韩国LG GN-5001RF 通用注塑级 注射成型
PC/ABS 韩国LG GN-5001SF-NP 通用注塑级
PC/ABS 韩国LG GN-5001TF 通用注塑级
PC/ABS 韩国LG GN-5007FM 通用注塑级
PC/ABS 韩国LG GN-5008HF 通用注塑级
PC/ABS 韩国LG GN-5009F 通用注塑级 阻燃
PC/ABS 韩国LG GN-5101RF 通用注塑级
PC/ABS 韩国LG GN-5151RFA 通用注塑级
PC/ABS 韩国LG GN-5151RFH 通用注塑级
PC/ABS 韩国LG GN-5301F 通用注塑级
PC/ABS 韩国LG GP-5008BF 通用注塑级
PC/ABS 韩国LG GP-5008BFH 通用注塑级
PC/ABS 韩国LG GP-5200 通用注塑级
PC/ABS 韩国LG GP-5206F 通用注塑级
PC/ABS 韩国LG GP-5300 通用注塑级
PC/ABS 韩国LG HI-5002A 通用注塑级
PC/ABS 韩国LG HR-5006A 通用注塑级
PC/ABS 韩国LG HR-5007A 通用注塑级
PC/ABS 韩国LG HR-5007AX 通用注塑级